Home > Filament > PLA Silk

PLA Silk

Basic Information

PLA is an environmentally friendly material, environmentally friendly, non-toxic and biodegradable with low shrinkage, no warping, no cracking, suitable for all models of FDM 3D printers, suitable for printing crafts, artwork, and industrial design samples.

Select Color

Physical Property

  • Resilience
  • Dissociation
  • Durometer
  • Stiffness
  • Printability
  • Z-axis strength

Path Specifications

Weight Specifications

FAQ

What should I do if the sump won't stick to the platform?
Tips 1:Re-leveling
Tips 2:Increase the exposure time of the bottom layer by 10-20s each time until the chassis can adhere more firmly to the platform;
How do I make sure the coil stays neat after use?
Tips 1:Re-leveling
Tips 2:Increase the exposure time of the bottom layer by 10-20s each time until the chassis can adhere more firmly to the platform;
What if the printed model is warped?
Tips 1:Re-leveling
Tips 2:Increase the exposure time of the bottom layer by 10-20s each time until the chassis can adhere more firmly to the platform;
How do I make sure the coil stays neat after use?
Tips 1:Re-leveling
Tips 2:Increase the exposure time of the bottom layer by 10-20s each time until the chassis can adhere more firmly to the platform;
What if the printed model is warped?
Tips 1:Re-leveling
Tips 2:Increase the exposure time of the bottom layer by 10-20s each time until the chassis can adhere more firmly to the platform;

Basic Physical Properties

THE K5TM PLA MPrinted parts (specimen horizontal printing, 100% line filling)Injection molded partTest standard
Densities(g/cm³)1.40-1.45
ISO1183
Melt index(MFR)13-5
ISO1133
Heat deflection temperature(HDD258
ISO75
Vicat softening temperature(VST)357
ISO306
Tensile strength(MPa)39
ISO527
Tensile elongation at break(%)3
Bending strength(MPa)78
ISO178
Bending modulus(MPa)2200
Unnotched impact strength of simply supported beams(K/m²)40
ISO179
Notched impact strength of simply supported beams(K/m²)8

*1.Test condition:temperature ()=220'C: Mass (m)=10kg.

*2.Test condition: bending stress=0.45MPa : Heating rate=120 °C/h.

*3.Test condition: load=10N ; Heating rate=120 °C/h.