Home > Filament > PLA Matte

PLA Matte

Basic Information

PLA is an environmentally friendly material, environmentally friendly, non-toxic and biodegradable with low shrinkage, no warping, no cracking, suitable for all models of FDM 3D printers, suitable for printing crafts, artwork, and industrial design samples.

Select Color

  • blue
  • colorful
  • red

Physical Property

  • Resilience
  • Dissociation
  • Durometer
  • Stiffness
  • Printability
  • Z-axis strength

Path Specifications

Weight Specifications

FAQ

What should I do if the sump won't stick to the platform?
Tips 1:Re-leveling
Tips 2:Increase the exposure time of the bottom layer by 10-20s each time until the chassis can adhere more firmly to the platform;
How do I make sure the coil stays neat after use?
Tips 1:Re-leveling
Tips 2:Increase the exposure time of the bottom layer by 10-20s each time until the chassis can adhere more firmly to the platform;
What if the printed model is warped?
Tips 1:Re-leveling
Tips 2:Increase the exposure time of the bottom layer by 10-20s each time until the chassis can adhere more firmly to the platform;
How do I make sure the coil stays neat after use?
Tips 1:Re-leveling
Tips 2:Increase the exposure time of the bottom layer by 10-20s each time until the chassis can adhere more firmly to the platform;
What if the printed model is warped?
Tips 1:Re-leveling
Tips 2:Increase the exposure time of the bottom layer by 10-20s each time until the chassis can adhere more firmly to the platform;

Basic Physical Properties

THE K5TM PLA MPrinted parts (specimen horizontal printing, 100% line filling)Injection molded partTest standard
Densities(g/cm³)1.40-1.45
ISO1183
Melt index(MFR)13-5
ISO1133
Heat deflection temperature(HDD258
ISO75
Vicat softening temperature(VST)357
ISO306
Tensile strength(MPa)39
ISO527
Tensile elongation at break(%)3
Bending strength(MPa)78
ISO178
Bending modulus(MPa)2200
Unnotched impact strength of simply supported beams(K/m²)40
ISO179
Notched impact strength of simply supported beams(K/m²)8

*1.Test condition:temperature ()=220'C: Mass (m)=10kg.

*2.Test condition: bending stress=0.45MPa : Heating rate=120 °C/h.

*3.Test condition: load=10N ; Heating rate=120 °C/h.